FEATURES

Clip: .008 Beryllium Copper half hard per QQ-C-533 heat treated full hard

Insulation:  Kynar Shrink Tubing per Mil-I-23053/8 Color: Blue. Insulator Tape meets Mil-I-15126

Plating:            

G: Gold plate per Mil-G-45204 Type II, Class I, .000050 min. over nickel plate per QQ-N-290 Class I, .00010 min.

GS: Gold plate per Mil-G-45204 Type II, Class O, .000030 min. over nickel plate per QQ-N-290 Class I, .00010 min.

T : Bright Tin per Mil-T-10727 Type I .00010 min.

Contact Resistance: Less then 10 milliohms

Vibration: 4 hours sinusoidal cycling in each of three major orthogonial axis over the frequency range of 10 to 2000 to Hz at a double amplitude of .06 inch up to a limit value of 15G peak.

Contact Resistance After Vibration Test:  Less than 10 milliohms.

Insulation Resistance:  More than 100,000 megohms at 500 VDC for 60 seconds.

Thermal Shock:  3 cycles of 30 minutes each at – 65 degrees C and + 105 degrees C.

Humidity:  10 cycles for a total of 240 hours, between + 25 degrees C and + 65 degrees C relative humidity 80% to 98%.

Insulation Resistance After Humidity Test: 10,000 megohms minimum, at 500 VDC for 60 seconds

Durability:  No wear after 100 cycles with gold plated pin bar, contact resistance less than 10 milliohms

 

 

Grid or pin pattern	Part No.	Terminal size	Y	X	W	V	U	R	Q	S	T
.100	6264	022X036 025 SQ	.089	.05	.125	.20	.10	.40	.30	.007 .012	.03
.125	6100	022X036 025 SQ	.100	.05	.125	.25	.12	.50	.38	.007 .012	.04
.150	6282	022X036 025 SQ	.125	.05	.125	.30	.15	.60	.45	.007 .012	.04
.200	6437A	045 SQ	.160	.06	.135	.40	.20	.60	.40	.020 .030	.05
.200	6437B	03 X 06	.160	.06	.135	.40	.20	.60	.40	.007 .017	.05
.200	6437C	06 X 03	.160	.06	.135	.40	.20	.60	.40	.030 .040	.05
.250	6281A	045 SQ	.160	.06	.135	.50	.25	.75	.50	.020 .030	.05
.250	6281B	03 X 06	.160	.06	.135	.50	.25	.75	.50	.007 .017	.05
.250	6281C	06 X 03	.160	.06	.135	.50	.25	.75	.50	.030 .040	.05